Sumitube® O2 |
|
|
|
Dual Wall Polyolefin, --
Operating Temperature: -55 up to 105°C |
|
|
|
ASTM D 2671
ISO 37
JASO M 104
JIS C 3005 |
|
Surface:
Glossy
Marking: None |
  |
|
|
Dimensions |
|
BEFORE SHRINKAGE |
AFTER SHRINKAGE |
DELIVERY UNITS
* |
|
Inner diameter
(EID) min. |
Inner diameter
(RID) max. |
Wall thickness
(RWT) min-max |
Unit quantity |
Box quantity |
|
[type] |
[mm] |
[mm] |
[mm] |
[m] |
[m] |
|
6 x 0,7 |
6,00 |
4,50 |
nom. 1,20 |
200 |
1000 |
|
9 x 0,6 |
9,00 |
6,10 |
nom. 1,20 |
100 |
500 |
|
11 x 0,7 |
11,0 |
7,90 |
nom. 1,30 |
100 |
500 |
|
* Sizes 10,3mm, 13mm, 14mm and 17mm are available upon request. Size 6/4,5 is also available as drum of 2200 m. |
|
|
Colours & Technical drawing |
|
|
|
|
SPECIAL COLOURS |
|
upon request |
|
|
|
|
TECHNICAL DRAWING |
|
 |
|
|
| |
©
2009 SUMITOMO
ELECTRIC Schrumpf-Produkte GmbH. Subject to change. Tube colours may vary. |
SUMITOMO-G-28062022 PM0809 |
|
|
|
|
Sumitube® O2 |
|
|
|
Dual Wall Polyolefin, -- |
|
|
|
|
|
Technical properties |
|
PHYSICAL PROPERTIES |
|
PROPERTY |
TEST METHOD |
REQUIREMENT |
TYPICAL VALUE |
|
Longitudinal Change |
ASTM D 2671 |
Max. ± 5% |
-1% |
|
Specific Gravity |
ASTM D 792 |
Max. 1,00 |
0,95 |
|
Tensile Strength |
ASTM D638 |
Min. 12 MPa |
≥ 18 MPa |
|
Elongation at Break |
ASTM D638 |
Min. 300% |
≥ 460% |
|
Impact Test (-30°C) |
JIS C 3005 |
no cracking |
Pass |
|
Stress Cracking Test (50°C x 24h) |
(immersion IGEPAL 10%) |
no growth |
Pass |
|
THERMAL PROPERTIES |
|
PROPERTY |
TEST METHOD |
REQUIREMENT |
TYPICAL VALUE |
|
Operating Temperature |
Life-Curve |
-55 up to 105°C |
-55 up to 105°C |
|
Min. Shrink Temperature |
Shrink curve |
full recovery |
115°C |
|
Shrinking starts at |
Shrink curve |
|
80°C |
|
Elongation after heat ageing (120°C x 24h) |
ASTM D638 |
Min. 270% |
≥ 500% |
|
Tensile Strength after heat ageing (120°C x 24h) |
ASTM D638 |
Min. 12 MPa |
≥ 14 MPa |
|
Heat Shock (200°C x 4h) |
ASTM D 2671 |
no crack, flowing or dripping |
Pass |
|
Brittle Point |
ASTM D 746 |
Max. -55°C |
-70°C |
|
Deformation Resistance (140°C x 10 min) |
(under 2 kg/cm2 x 5 min) |
Min. 60% |
≥ 75% |
|
CHEMICAL PROPERTIES |
|
PROPERTY |
TEST METHOD |
REQUIREMENT |
TYPICAL VALUE |
|
Water Absorption |
ISO 62 |
Max. 0,5% |
Pass |
|
OTHER PROPERTIES |
|
PROPERTY |
TEST METHOD |
REQUIREMENT |
TYPICAL VALUE |
|
Adhesion Strength Test * |
(T-peel on ALU-pipe at 23°C) |
Min. 10N/10mm |
≥ 20N/10mm |
|
Longitudinal Change * |
ASTM D 2671 |
0 to -10% |
-3% |
|
Cold Impact (-40°C) * |
DIN VDE 0472 |
no cracking |
Pass |
|
Cold Impact (-35°C x 4h) * |
(-30°C x 0,5h) |
no cracking |
Pass |
|
Salt Water Spray Test (3000h) * |
NF-X 41.002 |
no corrosion |
Pass |
|
Heat Shock (200°C x 20min) * |
ASTM D 2671 |
no crack, flowing or dripping |
Pass |
|
Chipping Resistance * |
JASO M104 |
no rust |
Pass |
|
Fluid Resistance (after immersion 23°C x 72h) * |
Impact-Test |
no cracking |
Pass |
|
Bending Test (5 x on 25mm dia.) * |
(Visual check within 20 sec) |
no cracking |
Pass |
|
Stickiness (tightness) (after 120°C x 20 min) * |
(Visual checking) |
Sticking on pipe, no peeling |
Pass |
|
Impact Test * |
(-30°C x 0,5h) |
no cracking |
Pass |
| * Tubing shrunk on metal pipe.
Fluids: H2SO4. NaCl. Brake fluids SAE 1703 and LHM. High Octane Gasoline. |
|
| |
©
2009 SUMITOMO
ELECTRIC Schrumpf-Produkte GmbH. Subject to change. Tube colours may vary. |